Table 2 Approximated zero shear...

Table 2

Approximated zero shear viscosity based on “Carreau-Yasuda” and the calculated weight-average molar mass based on equation (3) for all build cycles compared to the new powder (BC 0) (arithmetic mean values of three measurements with their standard deviation)

Build cycle	Zero shear viscosity, η₀ (Pa.s)	Weight-average molar mass, M_w (g/mol)
BC 0	1,344 ± 7	24,546 ± 36
BC 1	2,082 ± 4	27,766 ± 14
BC 2	2,812 ± 4	30,217 ± 11
BC 3	6,291 ± 4	37,912 ± 7
BC 4	13,220 ± 405	46,730 ± 404
BC 5	15,397 ± 241	48,782 ± 216
BC 6	18,940 ± 617	51,710 ± 477
BC 7	23,807 ± 112	55,155 ± 73
BC 8	27,437 ± 290	57,404 ± 171
BC 9	41,517 ± 840	64,507 ± 368

Build cycle	Zero shearviscosity, η₀ (Pa.s)	Weight-averagemolar mass, M_w (g/mol)
BC 0	1,344 ± 7	24,546 ± 36
BC 1	2,082 ± 4	27,766 ± 14
BC 2	2,812 ± 4	30,217 ± 11
BC 3	6,291 ± 4	37,912 ± 7
BC 4	13,220 ± 405	46,730 ± 404
BC 5	15,397 ± 241	48,782 ± 216
BC 6	18,940 ± 617	51,710 ± 477
BC 7	23,807 ± 112	55,155 ± 73
BC 8	27,437 ± 290	57,404 ± 171
BC 9	41,517 ± 840	64,507 ± 368

Source: Authors’ own work