Tensile test of the polylactic acid plasticized samples manufactured by additive manufacturing with both infill patterns in terms of tensile strength (σm), elongation at break (εb) and tensile modulus (Et)
| Reference | σm (MPa) | εb (%) | Et (MPa) |
|---|---|---|---|
| PLA-L | 68.7 ± 0.5 | 2.6 ± 0.1 | 3,224 ± 180 |
| 10TEC-L | 41.7 ± 1.4 | 1.9 ± 0.1 | 2,573 ± 91 |
| 20TEC-L | 14.2 ± 0.9 | 174.4 ± 19.7 | 368 ± 21 |
| PLA-T | 41.4 ± 2.4 | 1.8 ± 0.2 | 2,530 ± 149 |
| 10TEC-T | 24.3 ± 3.0 | 1.5 ± 0.3 | 2,384 ± 145 |
| 20TEC-T | 13.3 ± 1.7 | 27.3 ± 2.1 | 255 ± 13 |
| σm (MPa) | εb (%) | Et (MPa) | |
|---|---|---|---|
| 68.7 ± 0.5 | 2.6 ± 0.1 | 3,224 ± 180 | |
| 41.7 ± 1.4 | 1.9 ± 0.1 | 2,573 ± 91 | |
| 14.2 ± 0.9 | 174.4 ± 19.7 | 368 ± 21 | |
| 41.4 ± 2.4 | 1.8 ± 0.2 | 2,530 ± 149 | |
| 24.3 ± 3.0 | 1.5 ± 0.3 | 2,384 ± 145 | |
| 13.3 ± 1.7 | 27.3 ± 2.1 | 255 ± 13 |