Flexural test of the polylactic acid plasticized samples manufactured by additive manufacturing with the longitudinal pattern in terms of flexural strength (σf), deformation at yield point (εfM) and flexural modulus (Et)
| Reference | σf (MPa) | εfM (%) | Ef (MPa) |
|---|---|---|---|
| PLA-L | 101.8 ± 2.5 | 3.8 ± 0.2 | 3,094 ± 60 |
| 10TEC-L | 59.1 ± 3.1 | 3.5 ± 0.1 | 2,541 ± 215 |
| 20TEC-L | 12.0 ± 1.8 | 7.9 ± 0.5 | 224 ± 57 |
| 10TEC/PLA/10TEC-L | 77.7 ± 2.0 | 4.4 ± 0.1 | 2,914 ± 70 |
| 20TEC/PLA/20TEC-L | 18.1 ± 1.1 | 8.5 ± 0.6 | 384 ± 12 |
| PLA/10TEC/PLA-L | 74.0 ± 1.7 | 3.7 ± 0.3 | 2,875 ± 99 |
| 20TEC/10TEC/20TEC-L | 16.0 ± 0.5 | 8.1 ± 0.6 | 327 ± 10 |
| PLA/20TEC/PLA-L | 85.8 ± 1.9 | 4.0 ± 0.1 | 2,515 ± 73 |
| 10TEC/20TEC/10TEC-L | 55.6 ± 1.1 | 3.2 ± 0.4 | 2,005 ± 9 |
| σf (MPa) | εfM (%) | Ef (MPa) | |
|---|---|---|---|
| 101.8 ± 2.5 | 3.8 ± 0.2 | 3,094 ± 60 | |
| 59.1 ± 3.1 | 3.5 ± 0.1 | 2,541 ± 215 | |
| 12.0 ± 1.8 | 7.9 ± 0.5 | 224 ± 57 | |
| 77.7 ± 2.0 | 4.4 ± 0.1 | 2,914 ± 70 | |
| 18.1 ± 1.1 | 8.5 ± 0.6 | 384 ± 12 | |
| 74.0 ± 1.7 | 3.7 ± 0.3 | 2,875 ± 99 | |
| 16.0 ± 0.5 | 8.1 ± 0.6 | 327 ± 10 | |
| 85.8 ± 1.9 | 4.0 ± 0.1 | 2,515 ± 73 | |
| 55.6 ± 1.1 | 3.2 ± 0.4 | 2,005 ± 9 |