Main results for the polylactic acid plasticized samples manufactured by additive manufacturing with transversal pattern
| Reference | (°) | (°) | Rr (%) |
|---|---|---|---|
| PLA-T | 178.3 ± 1.0 | 68.8 ± 1.0 | 61.4 ± 0.6 |
| 10TEC-T | 178.8 ± 0.5 | 77.8 ± 1.0 | 56.5 ± 0.6 |
| 20TEC-T | 165.3 ± 1.0 | 102.8 ± 1.3 | 37.8 ± 1.1 |
| 10TEC/PLA/10TEC-T | 174.5 ± 0.6 | 85.3 ± 1.0 | 45.1 ± 0.5 |
| 20TEC/PLA/20TEC-T | 106.3 ± 1.0 | 40.5 ± 1.3 | 61.9 ± 1.5 |
| PLA/10TEC/PLA-T | 178.5 ± 0.6 | 33.0 ± 0.8 | 81.4 ± 0.5 |
| 20TEC/10TEC/20TEC-T | 104.5 ± 1.3 | 42.3 ± 0.4 | 59.4 ± 0.9 |
| PLA/20TEC/PLA-T | 177.8 ± 0.5 | 28.5 ± 1.3 | 84.0 ± 0.7 |
| 10TEC/20TEC/10TEC-T | 160.5 ± 1.3 | 29.5 ± 1.3 | 81.6 ± 0.9 |
| Rr (%) | |||
|---|---|---|---|
| 178.3 ± 1.0 | 68.8 ± 1.0 | 61.4 ± 0.6 | |
| 178.8 ± 0.5 | 77.8 ± 1.0 | 56.5 ± 0.6 | |
| 165.3 ± 1.0 | 102.8 ± 1.3 | 37.8 ± 1.1 | |
| 174.5 ± 0.6 | 85.3 ± 1.0 | 45.1 ± 0.5 | |
| 106.3 ± 1.0 | 40.5 ± 1.3 | 61.9 ± 1.5 | |
| 178.5 ± 0.6 | 33.0 ± 0.8 | 81.4 ± 0.5 | |
| 104.5 ± 1.3 | 42.3 ± 0.4 | 59.4 ± 0.9 | |
| 177.8 ± 0.5 | 28.5 ± 1.3 | 84.0 ± 0.7 | |
| 160.5 ± 1.3 | 29.5 ± 1.3 | 81.6 ± 0.9 |