Main thermomechanical properties of the additive manufactured samples with both infill patterns
| Reference | E’ at −40 °C (MPa) | E’ at 70 °C (MPa) | Tg (°C) |
|---|---|---|---|
| PLA-L | 2,205 ± 5 | 3 ± 1 | 62.5 ± 1.2 |
| 10TEC-L | 2,176 ± 6 | 1 ± 1 | 49.3 ± 0.8 |
| 20TEC-L | 2,147 ± 8 | 52 ± 4 | 28.4 ± 0.4 |
| PLA-T | 1,748 ± 8 | 2 ± 1 | 63.0 ± 0.9 |
| 10TEC-T | 1,721 ± 7 | 1 ± 1 | 50.6 ± 0.8 |
| 20TEC-T | 2,068 ± 7 | 51 ± 3 | 29.9 ± 0.6 |
| E’ at −40 °C (MPa) | E’ at 70 °C (MPa) | Tg (°C) | |
|---|---|---|---|
| 2,205 ± 5 | 3 ± 1 | 62.5 ± 1.2 | |
| 2,176 ± 6 | 1 ± 1 | 49.3 ± 0.8 | |
| 2,147 ± 8 | 52 ± 4 | 28.4 ± 0.4 | |
| 1,748 ± 8 | 2 ± 1 | 63.0 ± 0.9 | |
| 1,721 ± 7 | 1 ± 1 | 50.6 ± 0.8 | |
| 2,068 ± 7 | 51 ± 3 | 29.9 ± 0.6 |