Rheological characteristics of resins N1–N5
| Resin | Storage modulus, MPa | Tgel, s | Induction period, s | Shrinkage, (%) | Viscosity, mPa·s |
|---|---|---|---|---|---|
| N1 | 17.35 ± 0.68 | 12.00 ± 0.5 | 0 ± 0 | 4.5 ± 0.1 | 30703 ± 216 |
| N2 | 19.62 ± 0.76 | 1.75 ± 0.0 | 0 ± 0 | 9.0 ± 0.2 | 14081 ± 153 |
| N3 | 16.09 ± 0.54 | 3.75 ± 0.1 | 2 ± 0 | 14.5 ± 0.6 | 47 ± 2 |
| N4 | 16.50 ± 0.49 | 1.75 ± 0.0 | 0 ± 0 | 13.5 ± 0.5 | 176 ± 6 |
| N5 | 22.96 ± 0.82 | 1.75 ± 0.0 | 0 ± 0 | 12.5 ± 0.3 | 381 ± 18 |