Results of the tensile tests
| Experiment | Factors | |||||
|---|---|---|---|---|---|---|
| Layer thickness | Nozzle temperature | Oven temperature | Infill style | Raster angle | UTS [MPa] | |
| 1 | −1 | −1 | −1 | −1 | −1 | 62.50 |
| 2 | −1 | −1 | −1 | −1 | 0 | 62.16 |
| 3 | −1 | −1 | −1 | −1 | 1 | 63.67 |
| 4 | −1 | 0 | 0 | 0 | −1 | 62.99 |
| 5 | −1 | 0 | 0 | 0 | 0 | 64.48 |
| 6 | −1 | 0 | 0 | 0 | 1 | 62.09 |
| 7 | −1 | 1 | 1 | 1 | −1 | 68.96 |
| 8 | −1 | 1 | 1 | 1 | 0 | 68.52 |
| 9 | −1 | 1 | 1 | 1 | 1 | 65.04 |
| 10 | 0 | −1 | 1 | 0 | −1 | 63.50 |
| 11 | 0 | −1 | 1 | 0 | 0 | 63.81 |
| 12 | 0 | −1 | 1 | 0 | 1 | 64.44 |
| 13 | 0 | 0 | −1 | 1 | −1 | 69.50 |
| 14 | 0 | 0 | −1 | 1 | 0 | 71.37 |
| 15 | 0 | 0 | −1 | 1 | 1 | 68.95 |
| 16 | 0 | 1 | 0 | −1 | −1 | 67.72 |
| 17 | 0 | 1 | 0 | −1 | 0 | 65.51 |
| 18 | 0 | 1 | 0 | −1 | 1 | 65.79 |
| 19 | 1 | −1 | 0 | 1 | −1 | 67.92 |
| 20 | 1 | −1 | 0 | 1 | 0 | 66.90 |
| 21 | 1 | −1 | 0 | 1 | 1 | 66.11 |
| 22 | 1 | 0 | 1 | −1 | −1 | 62.10 |
| 23 | 1 | 0 | 1 | −1 | 0 | 63.29 |
| 24 | 1 | 0 | 1 | −1 | 1 | 60.88 |
| 25 | 1 | 1 | −1 | 0 | −1 | 52.14 |
| 26 | 1 | 1 | −1 | 0 | 0 | 66.76 |
| 27 | 1 | 1 | −1 | 0 | 1 | 56.13 |
| Experiment | Factors | |||||
|---|---|---|---|---|---|---|
| Layer thickness | Nozzle temperature | Oven temperature | Infill style | Raster angle | UTS [MPa] | |
| 1 | −1 | −1 | −1 | −1 | −1 | 62.50 |
| 2 | −1 | −1 | −1 | −1 | 0 | 62.16 |
| 3 | −1 | −1 | −1 | −1 | 1 | 63.67 |
| 4 | −1 | 0 | 0 | 0 | −1 | 62.99 |
| 5 | −1 | 0 | 0 | 0 | 0 | 64.48 |
| 6 | −1 | 0 | 0 | 0 | 1 | 62.09 |
| 7 | −1 | 1 | 1 | 1 | −1 | 68.96 |
| 8 | −1 | 1 | 1 | 1 | 0 | 68.52 |
| 9 | −1 | 1 | 1 | 1 | 1 | 65.04 |
| 10 | 0 | −1 | 1 | 0 | −1 | 63.50 |
| 11 | 0 | −1 | 1 | 0 | 0 | 63.81 |
| 12 | 0 | −1 | 1 | 0 | 1 | 64.44 |
| 13 | 0 | 0 | −1 | 1 | −1 | 69.50 |
| 14 | 0 | 0 | −1 | 1 | 0 | 71.37 |
| 15 | 0 | 0 | −1 | 1 | 1 | 68.95 |
| 16 | 0 | 1 | 0 | −1 | −1 | 67.72 |
| 17 | 0 | 1 | 0 | −1 | 0 | 65.51 |
| 18 | 0 | 1 | 0 | −1 | 1 | 65.79 |
| 19 | 1 | −1 | 0 | 1 | −1 | 67.92 |
| 20 | 1 | −1 | 0 | 1 | 0 | 66.90 |
| 21 | 1 | −1 | 0 | 1 | 1 | 66.11 |
| 22 | 1 | 0 | 1 | −1 | −1 | 62.10 |
| 23 | 1 | 0 | 1 | −1 | 0 | 63.29 |
| 24 | 1 | 0 | 1 | −1 | 1 | 60.88 |
| 25 | 1 | 1 | −1 | 0 | −1 | 52.14 |
| 26 | 1 | 1 | −1 | 0 | 0 | 66.76 |
| 27 | 1 | 1 | −1 | 0 | 1 | 56.13 |