Table 7 Yield strength( R p 0,2 ),...

Table 7

Yield strength(R_p_0,2), ultimate tensile strength (UTS), and elongation at fracture (A) from the 3D-printed specimens, MIM specimens, BASF data sheet, studies from Caminero et al. (2022), Obadimu et al. (2022), and Pellegrini et al. (2022)

Specimen	Infill density [%]	Infill type	Printing orientation	R_p_0,2 [MPa]	UTS [MPa]	A [%]
BASF	105	Lines	Flat x–y	251	561	53
BASF	105	Lines	Upright z	234	521	36
This study	105	Zig-zag	Flat x	233.3 ± 7.1	474.3 ± 7.2	23.5 ± 1.7
This study	105	Lines	Flat x	233.0 ± 0.1	486.5 ± 10.6	25.0 + 2.5
Caminero et al. (2022)	100	Concentric	Flat x	184.6 ± 4.9	495.1 ± 5.3	35.4 ± 1.2
Caminero et al. (2022)	100	Concentric	On-edge x	188.1 ± 5.2	497.3 ± 4.3	37.6 + 0.8
Obadimu et al. (2022)	100	Lines	Flat x	146.4	421.8	35.4
Pellegrini et al. (2022)	100	Lines	Flat x	125.7	405.2	45
			On-edge x	132.7	439.3	43
			Upright z	122.7	399.6	35
MIM				210.7 ± 3.5	583.0 ± 1.0	73.6 ± 0.9

Specimen	Infill density [%]	Infill type	Printing orientation	R_p_0,2 [MPa]	UTS [MPa]	A [%]
BASF	105	Lines	Flat x–y	251	561	53
BASF	105	Lines	Upright z	234	521	36
This study	105	Zig-zag	Flat x	233.3 ± 7.1	474.3 ± 7.2	23.5 ± 1.7
This study	105	Lines	Flat x	233.0 ± 0.1	486.5 ± 10.6	25.0 + 2.5
Caminero et al. (2022)	100	Concentric	Flat x	184.6 ± 4.9	495.1 ± 5.3	35.4 ± 1.2
Caminero et al. (2022)	100	Concentric	On-edge x	188.1 ± 5.2	497.3 ± 4.3	37.6 + 0.8
Obadimu et al. (2022)	100	Lines	Flat x	146.4	421.8	35.4
Pellegrini et al. (2022)	100	Lines	Flat x	125.7	405.2	45
			On-edge x	132.7	439.3	43
			Upright z	122.7	399.6	35
MIM				210.7 ± 3.5	583.0 ± 1.0	73.6 ± 0.9

Note:

Only the maximum average value obtained for each printing orientation is reported for the study from Pellegrini et al., (2022)

Source: Table by authors