Material properties of the printing filaments in this study
| Material | Density (g/cm3) | Tensile strength (MPa) | Young modulus (MPa) | Elongation at yield (−) | Melting temperature (°C) | Glass temperature (°C) |
|---|---|---|---|---|---|---|
| PLA | 1.24 | 66 | 3,027 | 0.07 | 145–165 | 57 |
| PCL | 1.1 | 45 | 350 | 0.15 | 58–60 | −60 |
| Material | Density (g/cm3) | Tensile strength (MPa) | Young modulus (MPa) | Elongation at yield (−) | Melting temperature (°C) | Glass temperature (°C) |
|---|---|---|---|---|---|---|
| PLA | 1.24 | 66 | 3,027 | 0.07 | 145–165 | 57 |
| PCL | 1.1 | 45 | 350 | 0.15 | 58–60 | −60 |