Specifications of metal-impregnated carbon CS in selected countries
| Manufacturer | Description | Density (g/cm3) | Electrical resistivity (µΩ·m) | Flexural strength (MPa) | Source |
|---|---|---|---|---|---|
| Mersen (P5696) | Metal impregnated (22% Cu) | 2.25 | 6 | 70 | Mersen (2024) |
| Mersen (P2805) | Metal impregnated (28% Cu) | 2.4 | 3.5 | 70 | Mersen (2024) |
| Mersen (P3210) | Metal impregnated (32% Cu) | 2.5 | 2.2 | 85 | Mersen (2024) |
| Morgan (MY131) | Metalised carbon light weight lead free | 2.2 | 8 | 60 | Morgan (2024) |
| Morgan (MY7A2) | Metalised carbon low resistivity for general applications lead free | 2.4 | 4 | 60 | Morgan (2024) |
| Morgan (MT85A) | Metalised carbon low resistivity for general applications lead free | 2.4 | 3 | 65 | Morgan (2024) |
| Morgan (MY258A2) | Metalised carbon low resistivity for high current applications lead free | 2.7 | 2 | 60 | Morgan (2024) |
| Morgan (MY258A4) | Metalised carbon low resistivity for high current applications lead free | 2.8 | 1 | 60 | Morgan (2024) |
| Pantrac (RH83M6) | Impregnated carbon | 3.4 | 7 | 102 | Pantrac (2024) |
| Elekro Karbon a.s. (SK162) | Metal impregnated (Cu) | 2.3 | 5 | 60 | Fadzil et al. (2023) |
| L. T graphite (PCS-30) | Metal impregnated (32% Cu) | 2.5 | 2.2 | 80 | L. T graphite (2024) |
| Morteng (CK20) | higher strength and lower resistivity | 2.7 | 5 | 75 | Morteng (2024) |
| Morteng (CK50) | carbon based material-impregnated material, good conductivity, strength, and density | 2.3 | 5 | 85 | Morteng (2024) |
| Morteng (CK80) | Carbon based metal impregnated material, less copper infiltration, relatively light | 2 | 8 | 80 | Morteng (2024) |
| Manufacturer | Description | Density (g/cm3) | Electrical resistivity (µΩ·m) | Flexural strength (MPa) | Source |
|---|---|---|---|---|---|
| Mersen (P5696) | Metal impregnated (22% Cu) | 2.25 | 6 | 70 | |
| Mersen (P2805) | Metal impregnated (28% Cu) | 2.4 | 3.5 | 70 | |
| Mersen (P3210) | Metal impregnated (32% Cu) | 2.5 | 2.2 | 85 | |
| Morgan (MY131) | Metalised carbon light weight lead free | 2.2 | 8 | 60 | |
| Morgan (MY7A2) | Metalised carbon low resistivity for general applications lead free | 2.4 | 4 | 60 | |
| Morgan (MT85A) | Metalised carbon low resistivity for general applications lead free | 2.4 | 3 | 65 | |
| Morgan (MY258A2) | Metalised carbon low resistivity for high current applications lead free | 2.7 | 2 | 60 | |
| Morgan (MY258A4) | Metalised carbon low resistivity for high current applications lead free | 2.8 | 1 | 60 | |
| Pantrac (RH83M6) | Impregnated carbon | 3.4 | 7 | 102 | |
| Elekro Karbon a.s. (SK162) | Metal impregnated (Cu) | 2.3 | 5 | 60 | |
| L. T graphite (PCS-30) | Metal impregnated (32% Cu) | 2.5 | 2.2 | 80 | |
| Morteng (CK20) | higher strength and lower resistivity | 2.7 | 5 | 75 | |
| Morteng (CK50) | carbon based material-impregnated material, good conductivity, strength, and density | 2.3 | 5 | 85 | |
| Morteng (CK80) | Carbon based metal impregnated material, less copper infiltration, relatively light | 2 | 8 | 80 |