Table 3

The strengthening components of the LB-PBF 316L and the estimated yield strength (yest) compared to the experimental yield strength

Condition/Temperature	$f_{s m a l l}$	$f_{l a r g e}$	$d_{s m a l l}$	$d_{l a r g e}$	$σ_{0}$ (MPa)	$σ_{s s}$ (MPa)	$σ_{G B}$ (MPa)	$σ_{D i s}$ (MPa)	$σ_{y_{e s t}}$ (MPa)	$σ_{y_{e x p}}$ (MPa)
As-built	0.1	0.9	4.6	38	15	96.6	87.06628	366.7	565.4	627
425 °C	0.13	0.87	5	45	15	96.6	84.89903	333.49	530.0	772
650 °C	0.22	0.78	7	39	15	96.6	94.03957	301.14	506.8	816
870 °C	0.22	0.78	8.4	68	15	96.6	77.06424	271.12	459.8	684
1,150 °C	0.28	0.72	9.2	73	15	96.6	79.81547	264.86	456.3	649

Condition/Temperature	$f_{s m a l l}$	$f_{l a r g e}$	$d_{s m a l l}$	$d_{l a r g e}$	$σ_{0}$ (MPa)	$σ_{s s}$ (MPa)	$σ_{G B}$ (MPa)	$σ_{D i s}$ (MPa)	$σ_{y_{e s t}}$ (MPa)	$σ_{y_{e x p}}$ (MPa)
As-built	0.1	0.9	4.6	38	15	96.6	87.06628	366.7	565.4	627
425 °C	0.13	0.87	5	45	15	96.6	84.89903	333.49	530.0	772
650 °C	0.22	0.78	7	39	15	96.6	94.03957	301.14	506.8	816
870 °C	0.22	0.78	8.4	68	15	96.6	77.06424	271.12	459.8	684
1,150 °C	0.28	0.72	9.2	73	15	96.6	79.81547	264.86	456.3	649