| Color, appearance | Tan, smooth |
| Unworked penetration | 250 |
| Worked penetration, 60X | 265 |
| Oil separation, 30hr at 100C | 4.5% |
| Evaporation, 24hr at 100C perASTM D-972 | 0.2% |
| Dropping point per ASTM D-2265 | 185 C |
| 0.91 g/cc | |
| Oxidation stability per ASTM D-942: | |
| a. Conditions | 100 hrs @ 100 C |
| b. Pressure drop | 26 kPa |
| Water Washout, 1hr at 38C per ASTM D-1264 | 4.5 % |
| Water washout, lhr at 80C per ASTM D-1264 | 11.7 % |
| Bearing rust test per ASTM D-1743 | Pass |
| Low temperature torque at -40C per ASTM D-1478: | |
| a. Starting torque | 708 gm-cm |
| b. Running torque, 10min | 413 gm-cm |
| c. Running torque, 1hr | 236 gm-cm |
| Four-ball wear per ASTM D-2266: | (1200RPM, 40kg, 75C, 1 hr) |
| Wear scar: | 0.50 mm |
| Cleanliness: | 10-34 microns 500 particles/cc max 35 microns or larger No particles |
| Color, appearance | Tan, smooth |
| Unworked penetration | 250 |
| Worked penetration, 60X | 265 |
| Oil separation, 30hr at 100C | 4.5% |
| Evaporation, 24hr at 100C perASTM D-972 | 0.2% |
| Dropping point per ASTM D-2265 | 185 C |
| 0.91 g/cc | |
| Oxidation stability per ASTM D-942: | |
| a. Conditions | 100 hrs @ 100 C |
| b. Pressure drop | 26 kPa |
| Water Washout, 1hr at 38C per ASTM D-1264 | 4.5 % |
| Water washout, lhr at 80C per ASTM D-1264 | 11.7 % |
| Bearing rust test per ASTM D-1743 | Pass |
| Low temperature torque at -40C per ASTM D-1478: | |
| a. Starting torque | 708 gm-cm |
| b. Running torque, 10min | 413 gm-cm |
| c. Running torque, 1hr | 236 gm-cm |
| Four-ball wear per ASTM D-2266: | (1200RPM, 40kg, 75C, 1 hr) |
| Wear scar: | 0.50 mm |
| Cleanliness: | 10-34 microns 500 particles/cc max 35 microns or larger No particles |