Influence of the L/A ratio on the LMG material permeation using method 1
| LMG material | Coarse-grained material | Permeation: l | |||
|---|---|---|---|---|---|
| Consistency =100 mm | Consistency =150 mm | ||||
| D max: mm | d 15: mm | L/A = 1.4 | L/A = 1.7 | L/A = 1.4 | L/A = 1.7 |
| 2 | 35 | 0.2 | 2.3 | 0.0 | 3.7 |
| 2 | 75 | 1.7 | 6.9 | 2.0 | 25.0a |
| 2 | 110 | 2.4 | 19.0 | 3.2 | 25.4a |
| 4 | 35 | 0.6 | 5.9 | 1.2 | 6.7 |
| 4 | 75 | 3.5 | 21.4 | 4.7 | 25.0a |
| 4 | 110 | 16.2 | 25.1a | 23.4 | 25.6a |
| LMG material | Coarse-grained material | Permeation: l | |||
|---|---|---|---|---|---|
| Consistency =100 mm | Consistency =150 mm | ||||
| L/A = 1.4 | L/A = 1.7 | L/A = 1.4 | L/A = 1.7 | ||
| 2 | 35 | 0.2 | 2.3 | 0.0 | 3.7 |
| 2 | 75 | 1.7 | 6.9 | 2.0 | 25.0 |
| 2 | 110 | 2.4 | 19.0 | 3.2 | 25.4 |
| 4 | 35 | 0.6 | 5.9 | 1.2 | 6.7 |
| 4 | 75 | 3.5 | 21.4 | 4.7 | 25.0 |
| 4 | 110 | 16.2 | 25.1 | 23.4 | 25.6 |
No LMG material left in the cylindrical steel container