Influence of D max on the LMG material permeation using method 1
| LMG material | Coarse-grained material | Permeation: l | |||
|---|---|---|---|---|---|
| L/A = 1.4 | L/A = 1.7 | ||||
| Consistency: mm | d 15: mm | D max = 2 mm | D max = 4 mm | D max = 2 mm | D max = 4 mm |
| 100 | 35 | 0.2 | 0.6 | 2.3 | 5.9 |
| 100 | 75 | 1.7 | 3.5 | 6.9 | 21.4 |
| 100 | 110 | 2.4 | 16.2 | 19.0 | 25.1a |
| 150 | 35 | 0.0 | 1.2 | 3.7 | 6.7 |
| 150 | 75 | 2.0 | 4.7 | 25.0a | 25.0a |
| 150 | 110 | 3.2 | 23.4 | 25.4a | 25.6a |
| LMG material | Coarse-grained material | Permeation: l | |||
|---|---|---|---|---|---|
| L/A = 1.4 | L/A = 1.7 | ||||
| Consistency: mm | |||||
| 100 | 35 | 0.2 | 0.6 | 2.3 | 5.9 |
| 100 | 75 | 1.7 | 3.5 | 6.9 | 21.4 |
| 100 | 110 | 2.4 | 16.2 | 19.0 | 25.1 |
| 150 | 35 | 0.0 | 1.2 | 3.7 | 6.7 |
| 150 | 75 | 2.0 | 4.7 | 25.0 | 25.0 |
| 150 | 110 | 3.2 | 23.4 | 25.4 | 25.6 |
No LMG material left in the cylindrical steel container