Influence of the particle size of the coarse-grained material on the LMG material permeation using method 1
| LMG material | Coarse-grained material | Permeation: l | |||||
|---|---|---|---|---|---|---|---|
| Consistency = 100 mm | Consistency = 150 mm | ||||||
| L/A | D max: mm | d 15 = 35 mm | d 15 = 75 mm | d 15 = 110 mm | d 15 = 35 mm | d 15 = 75 mm | d 15 = 110 mm |
| 1.4 | 2 | 0.2 | 1.7 | 2.4 | 0.0 | 2.0 | 3.2 |
| 1.4 | 4 | 0.6 | 3.5 | 16.2 | 1.2 | 4.7 | 23.4 |
| 1.7 | 2 | 2.3 | 6.9 | 19.0 | 3.7 | 25.0a | 25.4a |
| 1.7 | 4 | 5.9 | 21.4 | 25.1a | 6.7 | 25.0a | 25.6a |
| LMG material | Coarse-grained material | Permeation: l | |||||
|---|---|---|---|---|---|---|---|
| Consistency = 100 mm | Consistency = 150 mm | ||||||
| L/A | |||||||
| 1.4 | 2 | 0.2 | 1.7 | 2.4 | 0.0 | 2.0 | 3.2 |
| 1.4 | 4 | 0.6 | 3.5 | 16.2 | 1.2 | 4.7 | 23.4 |
| 1.7 | 2 | 2.3 | 6.9 | 19.0 | 3.7 | 25.0 | 25.4 |
| 1.7 | 4 | 5.9 | 21.4 | 25.1 | 6.7 | 25.0 | 25.6 |
No LMG material left in the cylindrical steel container