Table 1. Experimental programme Test *...

Table 1.

Experimental programme

Test*	Height: mm	Diameter: mm	Confinement: MPa	Initial relative density: %	Initial porosity: %	Voxel size: μm	Number of scans
TCXL†	24·2	10·7	0·1	46	35·2	15·57	18
TCR	22·3	10·1	7	47	35·0	N/A	N/A
TCX1	23·5	9·4	7	58	38·8	15·57	7
TCX2	23·3	9·9	7	54	38·4	15·50	6
TCX3	23·4	9·3	7	57	38·4	8·82	2

Test*	Height: mm	Diameter: mm	Confinement: MPa	Initial relative density: %	Initial porosity: %	Voxel size: μm	Number of scans
TCXL†	24·2	10·7	0·1	46	35·2	15·57	18
TCR	22·3	10·1	7	47	35·0	N/A	N/A
TCX1	23·5	9·4	7	58	38·8	15·57	7
TCX2	23·3	9·9	7	54	38·4	15·50	6
TCX3	23·4	9·3	7	57	38·4	8·82	2

TC, triaxial compression; X, with XCT; L, low confinement; R, reference test.

†

The results of test TCXL have already been presented in Andò et al. (2012), where the test was named COEA01.