Table 4.

Mechanical parameters of fibre-reinforced ductile composites under uniaxial compression

No.	f_c: MPa	ε₀: %	σ_p/f_c	E₀: GPa	ν₀	Toughness index
M1-0	67·0	0·462	0·21	25·3	0·199	1·63
M1-Mono	53·3	0·448	0·35	18·7	0·165	2·07
M1-Hy1	51·7	0·456	0·34	18·6	0·157	2·62
M1-Hy2	59·4	0·459	0·35	21·5	0·179	2·85
M1-Hy3	57·7	0·547	0·33	20·7	0·181	2·69
M2-0	49·9	0·438	0·27	16·2	0·155	1·37
M2-Mono	43·6	0·339	0·35	17·1	0·180	2·47
M2-Hy1	40·9	0·390	0·32	16·6	0·181	2·61
M2-Hy2	43·1	0·445	0·37	16·6	0·173	3·32
M2-Hy3	41·9	0·440	0·37	16·2	0·160	3·19
M3-0	15·8	0·279	0·37	9·53	0·150	1·65
M3-Mono	15·1	0·327	0·38	8·55	0·157	3·51
M3-Hy1	13·5	0·390	0·33	7·58	0·148	3·20
M3-Hy2	13·5	0·395	0·36	8·11	0·145	3·52
M3-Hy3	13·1	0·375	0·40	8·30	0·145	3·65

No.	f_c: MPa	ε₀: %	σ_p/f_c	E₀: GPa	ν₀	Toughness index
M1-0	67·0	0·462	0·21	25·3	0·199	1·63
M1-Mono	53·3	0·448	0·35	18·7	0·165	2·07
M1-Hy1	51·7	0·456	0·34	18·6	0·157	2·62
M1-Hy2	59·4	0·459	0·35	21·5	0·179	2·85
M1-Hy3	57·7	0·547	0·33	20·7	0·181	2·69
M2-0	49·9	0·438	0·27	16·2	0·155	1·37
M2-Mono	43·6	0·339	0·35	17·1	0·180	2·47
M2-Hy1	40·9	0·390	0·32	16·6	0·181	2·61
M2-Hy2	43·1	0·445	0·37	16·6	0·173	3·32
M2-Hy3	41·9	0·440	0·37	16·2	0·160	3·19
M3-0	15·8	0·279	0·37	9·53	0·150	1·65
M3-Mono	15·1	0·327	0·38	8·55	0·157	3·51
M3-Hy1	13·5	0·390	0·33	7·58	0·148	3·20
M3-Hy2	13·5	0·395	0·36	8·11	0·145	3·52
M3-Hy3	13·1	0·375	0·40	8·30	0·145	3·65