Oxide compositions of blend-forming components
| Aluminium oxide (Al2O3) | Calcium oxide (CaO) | Silicon dioxide (SiO2) | Iron oxide (Fe2O3) | Sodium oxide (Na2O) | Potassium oxide (K2O) | Titanium dioxide (TiO2) | Sulfur trioxide (SO3) | |
|---|---|---|---|---|---|---|---|---|
| Class G cement: atomic % | 1·0 | 71 | 17 | 5·0 | 0·34 | 1·2 | — | 3·6 |
| CAC#80: atomic % | 75·2 | 24·7 | — | 0·1 | — | — | — | — |
| CAC#51: atomic % | 45·1 | 49·7 | — | 2·8 | — | — | 2·4 | — |
| FAF: atomic % | 35 | 2·7 | 50 | 7·1 | 0·30 | 3·1 | 1·6 | — |
| Sodium metasilicate: wt% | — | — | 46·6 | — | 50·5 | — | — | — |
| Aluminium oxide (Al2O3) | Calcium oxide (CaO) | Silicon dioxide (SiO2) | Iron oxide (Fe2O3) | Sodium oxide (Na2O) | Potassium oxide (K2O) | Titanium dioxide (TiO2) | Sulfur trioxide (SO3) | |
|---|---|---|---|---|---|---|---|---|
| Class G cement: atomic % | 1·0 | 71 | 17 | 5·0 | 0·34 | 1·2 | — | 3·6 |
| CAC#80: atomic % | 75·2 | 24·7 | — | 0·1 | — | — | — | — |
| CAC#51: atomic % | 45·1 | 49·7 | — | 2·8 | — | — | 2·4 | — |
| FAF: atomic % | 35 | 2·7 | 50 | 7·1 | 0·30 | 3·1 | 1·6 | — |
| Sodium metasilicate: wt% | — | — | 46·6 | — | 50·5 | — | — | — |