Table 1 Results of testing the... | Emerald Publishing

Table 1

Results of testing the properties of low-phenyl silicone rubber

No.	Test items		Test result
1	Hardness (Shore A)	Room temperature	60
2	Hardness (Shore A)	Low temperature −50 °C	63
3	Tensile strength (MPa)	Room temperature	9.34
4	Tensile strength (MPa)	Low temperature −50 °C	9.63
5	Elongation at break	Room temperature	673%
6	Elongation at break	Low temperature −50 °C	650%
7	Tear strength (right angle, kN/m)	Room temperature	21.7
8	Tear strength (right angle, kN/m)	Low temperature −50 °C	30.1
9	100% Tensile strength (MPa)	Room temperature	0.58
10	100% Tensile strength (MPa)	Low temperature −50 °C	0.59
11	300% Tensile strength (MPa)	Room temperature	2.04
12	300% Tensile strength (MPa)	Low temperature −50 °C	2.71
13	Compression cold resistance coefficient (−50 °C, Compression ratio 20%)		0.73
14	Brittle temperature		No damage at −60 °C

No.	Test items		Test result
1	Hardness (Shore A)	Room temperature	60
2	Hardness (Shore A)	Low temperature −50 °C	63
3	Tensile strength (MPa)	Room temperature	9.34
4	Tensile strength (MPa)	Low temperature −50 °C	9.63
5	Elongation at break	Room temperature	673%
6	Elongation at break	Low temperature −50 °C	650%
7	Tear strength (right angle, kN/m)	Room temperature	21.7
8	Tear strength (right angle, kN/m)	Low temperature −50 °C	30.1
9	100% Tensile strength (MPa)	Room temperature	0.58
10	100% Tensile strength (MPa)	Low temperature −50 °C	0.59
11	300% Tensile strength (MPa)	Room temperature	2.04
12	300% Tensile strength (MPa)	Low temperature −50 °C	2.71
13	Compression cold resistance coefficient (−50 °C, Compression ratio 20%)		0.73
14	Brittle temperature		No damage at −60 °C

Source(s): Authors’ own work