The purpose of this paper is to study the variations of composition and properties of the passive film on 316 L stainless steel surface in 80°C, 0.5 mol L-1 H2SO4 + 2 mg L-1 NaF solution, is helpful to understand the mechanisms of corrosion resistancethe of plated Pd on 316 L ss.
The variations of composition and properties of the passive film on 316 L stainless steel surface in 80°C, 0.5 mol L-1 H2SO4 + 2 mg L-1 NaF solution after connected to Pd electrode were studied with methods of potential monitor, X-ray photoelectron spectroscopy analysis and electrochemical impedance spectrum (EIS) measurement.
By connecting to a Pd electrode, the potential of the SS sample increased from the active region to the passive region. By connecting to the Pd electrode, the contents of Cr, Cr(OH)3 and Fe3O4 in passive film increased obviously. With increased Pd/SS area ratio, the Cr(OH)3 content in passive film increased but the Fe3O4 content changed little. The results show that after connecting to Pd the corrosion resistance of the passive film on 316 L stainless steel increases obviously, which may be attributed to the more compact passive film because of higher Cr, Cr(OH)3 and Fe3O4 contents and less point defects in the film.
The effects and mechanism of Pd on passivation of SS was studied.