– This paper aims to present a correlation study on general and accelerated corrosion of the welded structure of aluminum alloy 2219 in N2O4.
– Corrosion experiments of the Tungsten Inert Gas (TIG)-welded aluminum alloy structure were conducted under both mild and accelerated corrosion conditions by changing the water content in N2O4.
– The experimental results indicated that both general and accelerated corrosion processes of the TIG-welded structure of aluminum alloy 2219 in N2O4 followed the linear equation ΔW = A + Bt, and the corrosion products were unchanged regardless of the water content in the N2O4 solution.
– The weight loss comparison method is used to identify the structure of the conventional aluminum welding and aluminum welding structure corrosion dinitrogen tetroxide in nitric acid accelerated corrosion relationship.