The purpose of this study is to investigate the effect of prior cold work after annealing and thermal ageing on intergranular corrosion or sensitization of Cr-Mn austenitic stainless steel (ASS) is necessary. Such a study is particularly important because ASS are mostly used and welded in mill-annealed condition, which is equivalent to fully annealed material with some cold worked (CW).
The effect of 15% CW of 202 ASS were investigated using microstructural (optical microscope), mechanical (grain size and hardness) and electrochemical methods (double loop electrochemical reactivation [DLEPR]) followed by thermal ageing (800°C, 900°C and 1000°C).
X-ray diffraction analysis shows the presence of martensite in CW samples. The increase in martensite formation (800°C and 900°C) can be observed with the variation of thermal ageing (TA) duration (1, 2 and 3 h). However, there was decreased in the formation of martensite at the temperature of 1000°C because of martensitic reversal. The DLEPR test result shows higher degree of sensitization (DOS) for 800°C and 900°C but for 1000°C, there was re-homogenization of samples which leads to lower DOS (thermal ageing for 1, 2 and 3 h).
For 300 series steel, there are various literature available for the effect of cold work on mechanical properties and DOS. However, no one has investigated the effect of cold work and thermal ageing on the sensitization of 202 Cr-Mn ASS.