This study aims to report the oxidation behaviors of the T91 ferritic/martensitic steel (T91 steel) and 304 austenitic stainless steel (304 steel) in supercritical water (SCW) at 600°C.
The microstructure, elemental distribution and phase structure of the oxidation layers derived from the corrosion of the T91 steel and 304 steel were analyzed by scanning electron microscopy, Oxford Instrument X-ray spectroscopy, electron scattered diffraction and transmission electron microscopy.
The oxidation layers on the T91 steel and 304 steel have duplex structure. The two steels all suffer internal oxidation, and the phase of the internal oxidation layers are indexed as Fe-Cr spinel, although their morphologies are different. The formation of a continuous Cr-rich layer is not detected because of the relatively low Cr content of the steels, which is attributed to the corrosion property.
The accelerated corrosion and corrosion mechanism of the T91 steel and 304 steel with low Cr occurring in SCW at 600°C was clarified.