This paper aims to compare the aging behavior of water-based coatings and solvent-based coatings in sulfuric acid environments and to discuss the related mechanism.
A sulfuric acid solution with a concentration of 5 Wt.% was selected for immersion test at 23°C. The failure behavior of the coating was studied by combining the transformation rules of the macroscopic morphology and basic properties with the results of electrochemical impedance spectrum analysis.
The results showed that the surface smoothness of the water-based coating was lower than that of the solvent-based coating. The glossiness, thickness and hardness of the water-based coating exhibited more significant changes. The electrochemical test also indicated that the water-based coating was infiltrated by a large number of corrosive media, which may have induced corrosion under the coating. In contrast, the solvent-based coating showed good shielding properties, but the adhesion was seriously affected by the corrosive medium.
This work clarified the difference of failure behavior and mechanism between water-based coatings and solvent-based coatings in acidic environment and provided a theoretical basis for the selection and mechanism research of anticorrosive coatings.