...Rihan Rihan; Nourah Alnajdi; Rachid Sablit; Mesferah Alqahtani; Surya Prakash Purpose The purpose of this study is to investigate the susceptibility of L80, and other steels with 1% Cr, 3% Cr and 9% Cr, to stress corrosion cracking ( SCC ), pitting, crevice and stress concentration effect...

...Jianwei Du; Hongliang Ming; Chen Wang; Jianqiu Wang Purpose Hydrogen embrittlement and stress corrosion cracking have been regarded as major threats to the safe operation of hydrogen transportation pipelines. This study aims to investigate their combined effects on the cracking behavior...

... Three new anchor bolt materials were designed around the 1Ni system. The stress corrosion cracking resistance of the new materials was characterized by microstructure observation, electrochemical testing and slow strain rate tensile testing. Findings The strength of the new anchor bolt materials has...

...Tingyun Ming; Qunjia Peng; Yaolei Han; Tao Zhang Purpose This paper aims to understand the effect of water jet cavitation peening (WJP) on stress corrosion cracking (SCC) behavior of alloy 600 and alloy 182 in high temperature water. Design/methodology/approach Surface and cross-section...

...Lin Chen; Huisheng Yang; Yanjing Su; Lijie Qiao Purpose The purpose of this study is to develop the existence and mechanism of stress corrosion cracking (SCC) for A517 steel in marine environments. Design/methodology/approach Slow strain rate test (SSRT) and constant load tests were used...

... tubing steel were tested, and met the API Spec 5CT standard. The fractures were investigated by scanning electron microscopy and energy dispersive spectroscopy. Findings Fracture was induced by stress corrosion cracking (SCC) and that the stress concentration caused by the mechanical damage played...

...Jing Liu; JiHao Cheng; Qian Hu; Feng Huang; JinQiao Xu; Bin Guo Purpose The purpose of this paper is to clarify the influence of the cathodic polarized potential on the stress corrosion cracking (SCC) susceptibility of X120 steel in a simulated acidic soil solution and the different SCC mechanisms...

...M. Askari‐paykani; M. Meratian; M. Shayan; K. Raeissi Purpose The purpose of this paper is to investigate the microstructural changes and stress corrosion cracking behavior via two‐stage stressing u‐bent tests for T6 and T73 tempers of Al 7075 Alclad alloy. Design/methodology/approach Study...