The purpose of this study is to investigate the microstructure of fretting wear behavior in 6061-T6 aluminum alloy. The fretting wear of blind riveted lap joints of 6061-T6 aluminum alloy plates, which are widely used in aircraft construction, was investigated. Fretting damages were investigated between the contact surface of the plates and between the plate and the rivet contact surface.
Experiments were carried out using a computer controlled Instron testing machine with 200 kN static and 100 kN dynamic load capacity. Max package computer program was used for the control of the experiments. Fretting scars, width of wear scars, microstructure was investigated by metallographic techniques and scanning electron microscopy.
It was found that fretting damages were occurred between the plates contacting surface and between the plate and rivet contact surface. As load and cycles increased, fretting scars increased. Fretting wear initially begins with metal-to-metal contact. Then, the formed metallic wear particles are hardened by oxidation. These hard particles spread between surfaces, causing three-body fretting wear. Fretting wear surface width increases with increasing load and number of cycles.
The useful life of many tribological joints is limited by wear or deterioration of the fretting components due to fretting by oscillating relative displacements of the friction surfaces. Such displacements are caused by vibrations, reciprocating motion, periodic bending or twisting of the mating component, etc. Fretting also tangibly reduces the surface layer quality and produces increased surface roughness, micropits, subsurface microphone.