The purpose of this paper is to present the influence of modifying the fabric surface made from basalt fibers by the magnetron sputtering of chromium and aluminum layers on its resistance to contact heat and comfort properties.
In order to modify the surface of basalt fabric, the process of physical deposition from the gas phase was used. It relies on creating a coating on a selected substrate by applying physical atoms, molecules or ions of specific chemical compounds. The trial of modification was carried out using the magnetron sputtering method due to the material versatility, application flexibility and ability to apply layers on substrates of various sizes and properties.
The findings obtained regarding the heat resistance to contact heat and thermal insulation (comfort) properties show different values depending on the type of metal deposited and the thickness of coating layer. It was found that the modification of basalt fabric surface at the micrometer level changes the tested parameters.
This paper presents the results of resistance to contact heat and thermal insulation properties only for the twill fabric made of basalt fiber. The surface modification of fabric was carried out using the chromium and aluminum of two values of layer thickness (1 and 5 µm).
So far, no tests have been carried out to modify the surface of fabric made from basalt fiber yarns using the magnetron sputtering method. In addition, it has not been studied, how the modification of fabric affects its resistance to contact heat and thermophysiological properties.