The paper aims to investigate the friction and wear properties of three surface-modified piston rings matched with a chromium-plated cylinder liner.
Samples were taken from the chromium-plated cylinder liner, Cr-Al2O3 ring, CrN ring and Mo ring. Tribo-tests were conducted on a reciprocating sliding tribometer under fully formulated engine oils. Friction coefficients and wear depths of three friction pairs were tested. Surface morphologies of cylinder liners and piston rings before and after test were analyzed.
Experimental results show that in the Cr-Al2O3 piston ring, scuffing occurred easily when matched with the chromium-plated cylinder liner; compared with the Mo ring, the CrN ring could decrease the wear depth of the piston ring from 2.7 to 0.2 μm, and the wear depth of cylinder liner remained; however, the friction coefficient increased from 0.113 to 0.123. The tribological performances of three surface-modified piston rings were significantly different when they matched with chromium-plated cylinder liner.
Chromium-plated cylinder liner and the three kinds of surface-modified piston rings have excellent friction and wear properties, respectively. However, according to the systematic characteristics of internal combustion (IC) engine tribology, only the appropriate cylinder liner–piston ring can improve the tribological performance of the IC engine. This paper reports the tribological performance of three surface-modified piston rings matched with a chromium-plated cylinder liner. The results can be used as reference for the design of high-power-density diesel engine.