The main aim of this paper was to study the self-lubricating behavior and failure mechanism of silver-rich solid film for in-depth analyzing of the friction and wear property of TiAl-10 wt. per cent Ag self-lubricating composite.
The friction and wear property of TiAl-10 wt. per cent Ag self-lubricating composite sliding against Si3N4 ball was tested under the testing conditions of ball-on-disk wear system. Field emission scanning electron microscopy and electron probe microanalyzer were used to analyze the surface morphology of silver-rich solid film. The main element contents were tested by energy dispersive spectroscopy. Silver phase on wear scar could be well identified using X-ray photo-electron spectroscopy. The theory calculation of shearing stress on wear scar was executed to discuss the local failure mechanism of silver-rich solid film. The lubricating role of silver was also discussed to analyze the anti-friction and anti-wear behavior of silver-rich solid film.
The friction coefficients and wear rates of TASC gradually reduced at 0-65 min, and approached to small values (0.31 in friction coefficient and 3.10×104 mm3N-1m-1 in wear rate) at 65-75 min. The excellent friction and wear behavior of TASC was mainly attributed to the lubricating property of silver-rich film at 65-75 min. At 12→20 N, surface shearing stress increased up to 146.31 MPa, and exceeded more than the shearing strength (125 MPa) of silver-rich film, which caused the propagating of fatigue crack and the destroying of silver-rich film, leading to high friction and severe wear.
It is important that the self-lubricating behavior and local failure of solid film is explored for further understanding the friction and wear property of TiAl alloys.