This study aims to introduce a novel technique which helped in quantifying the wear performance of a roller chain which was lubricated by using the palm oil-based hexagonal boron nitride (hBN) nanoparticles (nano-biolubricant).
The efficiency of the nano-biolubricant was evaluated by using a custom-made roller chain tribometer, at different resistance torque values at a constant speed and running time. Prior to the test, 2 different lubrication conditions were applied. The mass loss and elongation behaviour of a roller chain was selected as a degradation metric for monitoring the amount of the chain wear. The predominant wear mechanism of a roller chain was identified by surface morphological analysis.
Regardless of the lubrication conditions, the wear performance of the roller chain was significantly increased, at increasing resistance torque values. Higher wear was noted when the roller chain was lubricated using a nano-biolubricant, however, the wear curve showed a promising high chain life. The predominant wear mechanism involved is abrasive wear.
Although an increase in the elongation during running is based on the wear between the pins and roller, none of the earlier studies quantified the wear performance of a roller chain under differing lubrication conditions. Hence, for bridging the gap, this study described a new method for measuring the wear performance of the roller chain which was lubricated using the palm oil-based hBN nanoparticles or a nano-biolubricant.
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-02-2020-0061/