This paper aims to improve the wear resistance of titanium alloy using a high-hardness boride layer, which was fabricated on Ti6Al4V by a high-temperature boronizing process.
The boride layers on Ti6Al4V were obtained at 1000°C for 5–15 h. Scanning electron microscopy, energy dispersive analysis and X-ray diffractometer were used to characterize the properties of the boride layer. The tribological performance of the boride layer at room and elevated temperatures was investigated.
The X-ray diffraction analysis showed that the boride layers were a dual-phase structure of TiB and TiB2. When the boronizing time increased from 5 h to 15 h, the microhardness increased from 1192 HV0.5 to 1619.8 HV0.5. At 25°C and elevated temperatures, the friction coefficients of the boride layers were higher than that of Ti6Al4V. The wear track areas of T-5 at 200°C and 400°C were 2.5 × 10–3 and 1.1 × 10–3 mm2, respectively, which were 6.1% and 2.6% of that of Ti6Al4V, indicating boride layer exhibited a significant wear resistance. The wear mechanisms of the boride layer transformed from slight peeling to oxidative wear and abrasive wear as the temperature was raised.
The findings provide an effective strategy for improving the wear resistance of Ti6Al4V and have important implications for the application of titanium alloy in a high-temperature field.