With the rapid development of the pipeline transportation and exploitation of mineral resources, it is urgent requirement for the high-performance polymer matrix composites with low friction and wear to meet the needs of solid material transportation. This paper aims to prepare high-performance ultrahigh molecular weight polyethylene (UHMWPE) matrix composites and investigate the effect of service condition on frictional behavior for composite.
In this study, UHMWPE matrix composites with different content of MoS2 were prepared and the tribological performance of the GCr15/composites friction pair in various sliding speeds (0.025–0.125 m/s) under dry friction conditions were studied by ball-on-disk tribology experiments.
Results show that the frictional behavior was shown to be sensitive to MoS2 concentration and sliding velocity. As the MoS2 content is 2 Wt.%, composites presented the best overall tribological performance. Besides, the friction coefficient fluctuates around 0.21 from 0.025 to 0.125 m/s sliding speed, while the wear rate increases gradually. Scanning electron microscopy images, energy-dispersive spectroscopy and Raman Spectrum analysis present that the main wear mechanisms were abrasive and fatigue wear.
The knowledge obtained herein will facilitate the design of UHMWPE matrix composites with promising self-lubrication performances which used in slag transport engineering field.