This paper aims to regulate the oil retention rate and tribological properties of pored polytetrafluoroethylene (PPTFE) using polyvinyl alcohol (PVA)-based oil gel.
PPTFE was first prepared by using citric acid (CA) as an efficient pore-making agent. Subsequently, PVA and chitosan solution was introduced into the pores and experienced a freezing-thawing process, forming PVA-based gels inside the pores. Then, the PPTFE/PVA composite was impregnated with polyethylene glycol 200 (PEG200), yielding an oil-impregnated PPTFE/PVA/PEG200 composite.
It was found that the oil-impregnated PPTFE/PVA/PEG200 composite exhibited advanced tribological properties than neat PTFE with reductions of 53% and 70% in coefficient of friction and wear rate, respectively.
This study shows an efficient strategy to regulate the tribological property of PTFE using a PVA-based oil-containing gel.