The effects of rapid cooling by water quenching on the stiffness properties of fire-damaged concrete Available to Purchase

This paper reports the results of experimental research into assessing the fractured state of fire-damaged concrete under rapid cooling in an attempt to establish the effects of fire-fighting operations on the structural integrity of concrete buildings subject to a fire. The investigation was driven by the need to improve the material models used in predicting the fire resistance of concrete members or redesigning such members after a fire incident. The extent of damage was quantified using the stiffness damage test. The stiffness characteristics of 40 fired limestone concrete cores were determined from a series of quasi-static load—unload cycles. The strain energy dissipated in the specimen during such cycles provides a quantitative measure of the damage. The damage index is defined as the area of the hysteresis loop divided by the stress range. Other stiffness parameters, such as the initial and chord moduli of elasticity, were also determined. The extent of damage was also examined using ultrasonic pulse velocity (UPV) and dynamic modulus methods. Visual examination and scanning electron microscopy were also used to provide qualitative assessment. Quenching hot concrete with water was found to result in a reduction in the stiffness of fire-affected concrete over the entire range of temperatures investigated. The damage index for air-cooled concrete after firing to 320°C is at the same level as that for concrete heated to 220°C and cooled by quenching. The inference here is that the traditionally held view that 300°C marks the onset of significant damage in concrete is debatable. UPV measurements confirmed the damaging effect of rapid cooling on the stiffness properties of fire-affected concrete. A further 10% reduction of the UPVof quenched concrete compared to air-cooled concrete was observed. The dynamic modulus measurement also confirmed the adverse effect of quenching on the modulus of elasticity of fired concrete.