Fire can severely affect concrete structures and with knowledge of the properties of materials, the damage can be assessed. Aggregate, cement matrix and their interaction are the most important components that affect concrete behaviour at high temperatures. The effect of incorporating recycled concrete aggregate or cementitious materials, namely, cement type and pulverized fly ash, are reviewed to provide a better understanding of their involvement in fire resistance.
More investigation research is needed to understand the fire resistance of such sustainable concrete that was already constructed. The present study illustrates the effect of using recycled concrete aggregate and cementitious materials on the fire resistance of concrete. To do so, a literature review was conducted and relevant data were collected and presented in a simple form. The author's selected research findings, which are related to the presents study, are also presented and discussed.
Recycled concrete aggregate enhances the concrete behaviour at high temperatures when it substitutes the natural aggregate by reasonable substitution (more than 25–30%). It also almost eliminates the possibility of spalling. Moreover, utilizing both supplementary cementitious materials with recycled concrete aggregate can improve the fire resistance of concrete. The incorporation of pulverized fly ash and slag in Portland cement or blended cement can generally keep the mechanical properties of concrete at a higher level after heating to a high temperature.
Recycled concrete aggregate enhances the concrete behaviour at high temperatures when it substitutes the natural aggregate by reasonable substitution (more than 25–30%). It also almost eliminates the possibility of spalling. Moreover, utilizing both supplementary cementitious materials with recycled concrete aggregate can improve the fire resistance of concrete. The incorporation of pulverized fly ash and slag in Portland cement or blended cement can generally keep the mechanical properties of concrete at a higher level after heating to a high temperature.