Studies of luminescence property of long afterglow Eu²⁺, Dy³⁺ activated Sr₂MgSi₂O₇ phosphor

Long afterglow Sr₂MgSi₂O₇ (SMS) phosphor was prepared by Douby's methods at high temperature and reductive atmosphere. The excitation and emission spectra of this phosphor showed that both had broad bands and that the main emission peak at 469 nm was due to 4f‐5d transitions of Eu⁺² and implied that the luminescence centres Eu⁺² occupied the Sr⁺² sites in the Sr₂MgSi₂O₇ host. The phosphor doped only with Eu ions did not demonstrate the long afterglow phenomenon, but when co‐doped with Dy⁺³ ions in the SMS matrix, significant long afterglow was observed.