Pigments with Ti^4 + −Zn^2 +, Ca^2 +, Sr^2 +, Mg^2 +‐based on mixed metal oxides with spinel and perovskite structures for organic coatings

The purpose of this paper is to synthesise X₂TiO₄ spinel‐type anticorrosion pigments and YTiO₃, perovskite‐type anticorrosion pigments, where X = Zn, Mg, Ca, Sr; Y = Ca for metal protective paints.

Anticorrosion pigments were synthesised from oxides or carbonates at high temperature. The following pigments were synthesised: TiO₂ · ZnO, 2TiO₂ · ZnO, TiO₂ · 2ZnO, TiO₂ · MgO, TiO₂ · CaO, TiO₂ · ZnO · MgO, and TiO₂ · ZnO · SrO. The pigments obtained were characterised by means of X‐ray diffraction analysis, measurement of particle sizes and scanning electron microscopy. The anticorrosion pigments synthesised were used to produce epoxy coatings with PVC = 10 per cent for each synthesised pigment. The coatings were tested for physical‐mechanical properties and in corrosion atmospheres. The corrosion test results were compared with those of alumino zinc phosphomolybdate.

A spinel or perovskite structure was found in the pigments synthesised. High anticorrosion efficiency was identified in all the synthesised pigments, the highest efficiency being demonstrated in the TiO₂ · ZnO pigment of spinel structure and in the TiO₂ · CaO pigment of perovskite structure.

The pigments synthesised can be conveniently used to protect metal bases from corrosion.

The use of pigments synthesised in anticorrosion coatings for metal protection presents a new approach. Its benefits are the use and the method of synthesising the anticorrosion pigments that do not contain heavy metals and that are acceptable for the environment.