Urethane Acrylate Oligomer with 100% solids was synthesised and characterised in order to study the application in electron beam curing with varying ratio of Trimethylol propane triacrylate (TMPTA). The purpose of this paper is to study effect of TMPTA addition on the crosslink density and different coating properties.
Polyester polyol was synthesised by reacting single diacid, adipic acid (AA), with Pentaerythritol (PENTA) and 1,6‐hexanediol (HD). Further, Urethane acrylate resin was synthesised by using Isophorone diisocyanate (IPDI), hydroxy ethyl acrylate (HEA) and Polyester polyol. The polyester polyol and urethane acrylate oligomer were characterised by 1H NMR, 13C NMR, FTIR and GPC. Further, TMPTA was added as a crosslinker to the urethane acrylate oligomer and cured by electron beam radiation. The cured UA films having varying concentration of TMPTA were employed to evaluate thermal property, contact angle analysis, mechanical and chemical properties.
The obtained results showed improvement in their chemical properties, mechanical properties, thermal properties and water contact angle at 20% of TMPTA iconcentration. The TMPTA also reduced the dose required for the curing.
The resin can be synthesised from different isocyanates as TDI, MDI and HMDI, etc. The study can also be done with different multi or mono functional monomers such as methacrylate, hexanediol diacrylate, ethylene glycol diacrylate, etc.
The paper provides the better solution to reduce the cost of the electron beam radiation required for the curing.
The method presented in the paper could be very useful for controlling environmental pollution; as the conventional method of curing releases volatile organic compounds (VOC).
In this paper, urethane acrylate and TMTPA cured with electron beam are shown to offer good coating properties. A high‐solid urethane acrylate coating would find numerous industrial applications in surface coatings.