Formability is an important property of automotive pre-coated metals (PCMs). The purpose of this study is to investigate the effect of long alkyl chains of polycarbonatediol to control the formability of polyester coatings.
Polyester resins with long alkyl chains were synthesized using different contents of polycarbonatediol. These resins were characterised by gel permeation chromatography (GPC), 1H nuclear magnetic resonance (1H NMR) and fourier transform infrared spectroscopy (FT-IR). The polyester coatings were characterised according to their viscoelastic behaviour, formability, flexibility and anti-corrosion property.
The tensile strength of PCM should be larger than 5.6 MPa of the compressive stress at a strain of 23.4 per cent to overcome the harsh condition of deep drawing. To analyse the formability, Fε (forming coefficient based on strain) and FU (forming coefficient based on strain energy) were calculated. When Fε and FU were larger than 1, the polyester coatings exhibited good formability.
Long alkyl chains of polycarbonatediol gave flexibility and good formability to the polyester coatings.
There are two conditions that lead to the good formability of PCM. One is tensile strength and the other is forming coefficients based on strain and strain energy.
Long alkyl chains of polyester were a major factor to improve flexibility and formability. Thus, to have good formability, the tensile strength of PCM should be larger than 5.6 MPa, and the forming coefficients should be larger than 1.