This paper aims to investigate the corrosion inhibition efficiency of Landolphia heudelotii (LH) on mild steel in 1 M HCl and 0.5 M H2SO4 using weight loss and potentiodynamic polarization techniques.
Water extract of LH was used as corrosion inhibitor on mild steel in acidic media at room temperature and elevated temperatures (30-60°C). Various concentrations of the plant extract were prepared from the stock solution obtained after solvent extraction. The inhibition efficiency of LH extract was evaluated and mechanism of adsorption was deduced.
LH extract showed significant corrosion inhibition on mild steel in both acidic media, with inhibition efficiency increasing with extract concentration. Potentiodynamic polarization measurements revealed mixed inhibition mechanism. Optimum inhibition efficiency was recorded at 2500 mg/L after 288 h. Mechanism of adsorption was mainly of physisorption. The inhibitor exhibited good inhibition efficiency even at elevated temperature.
This study provides new data on the anticorrosion characteristics of LH extract under the specified conditions. Further studies could expand the experimental variables and use advanced surface probe techniques.
The developed inhibitor provides an alternative method of inhibiting corrosion on mild steel using eco-friendly materials from natural products which are less toxic, safer, cost-effective and readily available.
The method used was effective and the inhibitor developed can be incorporated in surface coatings where mild steel is used as construction materials, as tube sheets, rods and bars.