The purpose of this study is to develop a multifunctional coating layer based on nitrocellulose (NC)/acrylic resins containing precipitated silica and kaolin and investigate its suitability for use in packaging applications.
Different loading levels (1 and 5 Wt.%) of precipitated silica or kaolin particles were incorporated into NC/acrylic-based coating formulations and applied on low-density polyethylene (LDPE) films. The coatings and coated LDPE films were characterized in terms of structural, physical, mechanical, thermal, optical, surface, morphological and water vapor barrier properties.
The glossiness of the coating formulations decreased by increasing the precipitated silica and kaolin content. The incorporation of kaolin (1 and 5 Wt.%) and precipitated silica (1 Wt.%) had no significant effect on the melting temperature of LDPE film; however, with the addition of 5 Wt.% precipitated silica, the melting and crystallization temperatures were significantly changed. The incorporation of 5 Wt.% precipitated silica and kaolin also enhanced the water vapor barrier properties of LDPE films. The light transmittance declined with the precipitated silica and kaolin addition, especially in the ultraviolet (UV)-A/UV-B spectrum regions indicating an excellent UV light protection.
It was concluded that NC/acrylic resins coatings containing precipitated silica and kaolin exhibit improved thermal stability, UV and water vapor barrier properties and have the potential for use in packaging applications.