The purpose of this study is to explore the interfacial adhesion between superhydrophobic coatings FC-X (X = 1%, 2%, 3%, 4% and 5%) and the concrete substrate, along with the impact of FC-X on the water repellency characteristics of the concrete substrate.
One synthetic step was adopted to prepare novel F-SiO2 NP hybrid fluororesin coating. The impact of varying mass fractions of F-SiO2 NPs on the superhydrophobicity of FC-X was analyzed and subsequently confirmed through water contact angle (WCA) measurements. Superhydrophobic coatings were simply applied to the concrete substrate using a one-step spraying method. The interfacial adhesion between FC-X and the concrete substrate was analyzed using tape pasting tests and abrasion resistance measurements. The influence of FC-X on the water repellency of the concrete substrate was investigated through measurements of water absorption, impermeability and electric flux.
FC-4% exhibits excellent superhydrophobicity, with a WCA of 157.5° and a sliding angle of 2.3°. Compared to control sample, FC-X exhibits better properties, including chemical durability, wear resistance, adhesion strength, abrasion resistance, water resistance and impermeability.
This study offers a thorough investigation into the practical implications of enhancing the durability and water repellency of concrete substrates by using superhydrophobic coatings, particularly FC-4%, which demonstrates exceptional superhydrophobicity alongside remarkable chemical durability, wear resistance, adhesion strength, abrasion resistance, water resistance and impermeability.
Through the examination of the interfacial adhesion between FC-X and the concrete substrate, along with an assessment of FC-X’s impact on the water repellency of the concrete, this paper provides valuable insights into the practical application of superhydrophobic coatings in enhancing the durability and performance of concrete materials.