The aim of this study is to optimize the electrospinning parameters used in the production process of polyvinyl chloride (PVC) nanofibers.
The response surface methodology (RSM) was used to determine the experimental design. The 30 nanofiber prototypes candidates were electrospun using a needle-based electrospinning machine. PVC polymer, N-dimethyl formamide and tetrahydrofuran solvents were used to prepare the electrospinning solution.
The electrospun nanofibers had a mean diameter of 386 ± 136.57 nm, in the range of 200−412 nm. The mean porosity was 31.60 ± 6.37% in the range of 15.33−41.53%. The webs made from electrospun nanofibers had a mean pressure loss of 194.23 ± 47.7 pa in the range of 124−300 pa. The highest statistically significant correlation was observed between solution concentration and nanofiber diameter (r = 0.756, p < 0.05).
The optimal electrospinning parameters were determined to be: a solution concentration of 11 weight percent, a voltage of 16.5 kV, a needle-collector distance of 13.5 cm and an electrospinning duration of 4 h.