Adhesive bonding is critical to the effectiveness and structural integrity of 3D printed components. The purpose of this study is to investigate the effect of joint configuration on failure loads to improve the design and performance of single lap joints (SLJs) in 3D printed parts.
In this study, adherends were fabricated using material extrusion 3D printing technology with polyethylene terephthalate glycol (PETG). A toughened methacrylate adhesive was chosen to bond the SLJs after adherend printing. In this study, response surface methodology (RSM) was used to examine the effect of the independent variables of failure load, manufacturing time and mass on the dependent variable of joint configuration; adherend thickness (3.2, 4.0, 4.8, 5.6, 6.4, and 7.2 mm) and overlap lengths (12.7, 25.4, 38.1, and 50.8 mm) of 3D printed PETG SLJs.
The strength of the joints improved significantly with the increase in overlap length and adherend thickness, although the relationship was not linear. The maximum failure load occurred with a thickness of 7.2 mm and an overlap of 50.8 mm, whilst the minimum failure load was determined with a thickness of 3.2 mm and an overlap of 12.7 mm. The RSM findings show that the optimum failure load was achieved with an adherend thickness of 3.6 mm and an overlap length of 37.9 mm for SLJ.
This study provides insight into the optimum failure load for 3D printed SLJs, reducing SLJ production time and mass, producing lightweight structures due to the nature of 3D printing, and increasing the use of these parts in load-bearing applications.