CORROSION FATIGUE Study of basic mechanism. An extensive study to determine the basic mechanism of corrosion fatigue has been conducted in Russia by the Central Scientific Research Institute of the Ministry of Railways, U.S.S.R. Measurements of local electrical potentials showed that stresses do not lower the potential at the points of stress concentration. A potential drop in the most stressed portion of specimens was observed only after prolonged stressing.