This study/paper aims to investigate the erosion wear performance of Ni-based coatings [Ni-Cr-O and NiCrBSiFe-WC(Co)] under sand-water slurry conditions.
A high-velocity oxy-fuel (HVOF) process was used to deposit the Ni-based coatings [Ni-Cr-O and NiCrBSiFe-WC(Co)] on the surface of stainless steel (SS 316L) substrate. A Ducom TR-41 erosion tester was used to conduct the tribological experiments on bare/HVOF coated SS 316L. The erosion wear experiments were carried out for different time durations (1.30-3.00 h) at different impact angles (0-60°) by running the pot tester at different rotational speeds (600-1,500 rev/min). The solid concentration of sand slurry was taken in the range of 30-60 Wt.%. The surface roughness of Ni-based coated surfaces was also measured along the transverse length of the specimens.
Results show the arithmetic mean roughness (Ra) values of Ni-Cr-O and NiCrBSiFe-WC coated SS-316L were 7.04 and 6.67 µm, respectively. The erosion wear SS-316L was almost 3.5 ± 1.5 times greater than that of the NiCrBSiFe-WC coatings. NiBCrSi-WC(Co) sprayed SS-316L showed lower erosion wear than Ni-Cr-O sprayed SS-316L. Microscopically, the eroded Ni-Cr-O coating underwent plowing, microcutting and craters. Ni-Cr-O coating have shown the ductile nature of erosion wear mechanism. NiBCrSi-WC(Co) surface underwent craters, plowing, carbide/boride pullout, fractures and intact. Erosion wear mechanisms on the eroded surface of NiBCrSi-WC(Co) were neither purely ductile nor brittle.
It is a useful technique to estimate the erosion wear of hydraulic machinery coated with Ni-based coatings imposed under mining conditions.
The erosion wear performance of HVOF-sprayed Ni-Cr-O and NiCrBSiFe-WC(Co) powders was investigated through extensive experimentation, and the results are well supported by scanning electron micrographs and 3D topology.