The aim of this paper is to conduct a real time evaluation of polypyrrole as an anti‐corrosive pigment in epoxy polyamide coating.
This study deals with synthesis of polypyrrole (PPy) by chemical oxidative polymerisation in laboratory conditions. The synthesised PPy was characterised by employing FT‐IR, XRD, SEM and EDX analysis. Epoxy film of bisphenol type hardened with polyamide based curing agent was used as the binder. PPy was used as anti‐corrosive pigment in concentrations varying from 0 to 5 wt% in the coating. In addition to anti‐corrosive property, mechanical, chemical and weathering properties of the coating containing PPy were studied and compared with epoxy polyamide coating without PPy.
The result obtained through various tests showed that the coating with 1 and 2% PPy exhibited excellent weathering resistance, mechanical properties and improved chemical resistance.
The anti‐corrosion property of the coating can be tested by means of atmospheric exposure such as Florida test or by means of electrochemical impedance spectroscopy.
The results find application in anti‐corrosive paints for industrial application.
This research paper presents the results of anti‐corrosion behaviour of PPy in epoxy‐polyamide coating. Based on this result, a highly effective anti‐corrosive coating can be formulated by addition of small percentage of PPy in combination with other conventional pigments, thereby enhancing corrosion protection.