The purpose of this study was to fabricate carbon nanotubes (CNT)-reinforced chromium oxide coatings and investigate mechanical and microstructural properties of these newly developed coatings on the boiler tube steel.
1 and 4 Wt.% CNT-reinforced Cr2O3 composite coatings were prepared and successfully deposited on ASTM-SA213-T22 (T22) boiler tube steel substrates using high-velocity oxy fuel (HVOF) thermal spraying method. Microhardness, porosity, metallography, X-ray diffraction (XRD), scanning electron microscopy (SEM)/energy-dispersive X-ray spectroscopy, cross-sectional elemental analysis and X-ray mapping analysis have been used to examine the coated specimens.
The porosity of the CNT-Cr2O3 composite coatings was found to be decreasing with the increases in CNT content, and hardness has been found to be increasing with increase in percentage of CNT in the composite coatings. The CNT were able to increase hardness by approximately 17 per cent. It was found that the CNT were uniformly distributed throughout Cr2O3 matrix. The CNT were found to be chemically inert during the spraying process.
It must be mentioned here that studies related to fabrication of HVOF sprayed CNT reinforced Cr2O3 composite coatings on T22 boiler tube steel are not available in the literature. Hence, present investigation can provide valuable information related to fabrication and properties of CNT reinforced coatings on boiler steel.