This study aims to analyze the wettability of the self-developed Sn–Bi–Zn solder and to conduct a series of analysis on the wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–Bi–Zn solder on Cu substrate.
The wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–Bi–Zn solder on Cu substrate were analyzed by experiments. The interface was observed by scanning electron microscope to study the effect of Zn content on its interface.
With the increase in brazing temperature, the final spreading equivalent radius of the solder increases significantly, and the final contact angle of the solder decreases significantly. In addition, when the Zn content is 1%, the spreading effect of solder is the best, the equivalent radius is the largest and the contact angle is the smallest. According to the microstructural analysis, the thick intermetallic compounds layer of the Sn–15Bi–xZn solders on the Cu substrate can be effectively decreased by adding appropriate Zn content.
The wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–15Bi–xZn solder on Cu substrate at different temperatures have not been studied yet.